Marine plywood for construction

Publish Time:
2019-05-29 11:22:46
VIEWS:
1138counts

Product Description

The marine plywood is made using much more durable face and core veneers, allowing it to perform longer in wet conditions and resist fungal attacks. This makes the marine plywood ideal for use on coastal areas, or onboard ships, where the plywood is constantly expose to humidity. The marine plywood is bonded using Type A phenolic bond, making it structurally stronger than the other variants of plywood. The marine plywood is considered one of the best variants of plywood in terms of surface finishing, ply count and durable


Instructions
size:1220mmx2440mm, 1250mmx2500mm, 1500mmx3050mm,2000x5000mm
Materia:Okoume,eucalyptus,and so on.
Cover: Okoume,eucalyptus,and so on
Glue:WBP, phenolic 72hours
Thickness:18mm-28MM
 

BS1088         


BS 1088 is the British Standard for Marine plywood that applies to plywood produced with untreated tropical hardwood veneers that have a set level of resistance to fungus and water. The plies are bonded with Weather Boil Proof (WBP) glue. Normally the highest standards of WBP glue is Dynea resin from Norway.

Although bs1088 is a British Standard, the gaboon plywood does not have to be manufactured in Britain as long as the final products comply with the standard. The standard is associated with Lloyd’s Register since it performs testing of products to this standard.


WBP Glue Line

BS 1088 plywood must use an adhesive, which has been proven to be highly resistant to weather, micro-organisms, cold and boiling water, steam and dry heat.


Face Veneers

The face veneers must be free of knots other than “sound pin” knots, of which there shall be no more than six(6) in ANY area of one square foot. There can be no more than an AVERAGE of two such knots per square foot over the entire surface. The veneers must be reasonably free from irregular grain. The use of edge joints is limited, and end joints are not allowed.


Core Veneers

Core veneers have the same basic requirements as face veneers, except that small splits are allowed, and there is no limit on the number of pin knots or edge joints. However, end joints are not allowed.


Limits of Manufacturing Defects

Defective bonds, pleats and overlaps, and gaps in faces are not permitted. Occasional gaps may be repaired using veneer inserts bonded with the proper resin.


Moisture Content

BS 1088 plywood must have a moisture content 6% – 14% when it leaves the mill.


Thickness Tolerances

4 mm +.02/-0.6 ; 6 mm +.04/-0.65 ; 9 mm +.06/-0.75 ; 12 mm +.09/-0.82
15 mm +.1/-0.9 ; 18 mm +.12/-0.98 ; 22 mm +.16/-1.08 ; 25 mm +1.8/-1.16


Face Veneer thickness

For any three-ply construction, which applies to 3 and 4 mm material, each face veneer shall be not thinner than 1/8 of the total thickness of veneers assembled dry.

Multi-Ply Construction– This applies to boards thicker than 4.8 mm (3/16″)

Each face veneer shall be a minimum of 1.3 mm and not thicker than 3.8 mm.
Each core veneer shall be no thicker than 4.8 mm




Certification

· ISO 9000 Management System Certificate

· CARB (California Air Resources Board)

· EN-13986 CE-Mark

· Certificates of FSC conformance

· Certificates of origin GSP Form A




* on demand

For more information, please CONTACT us.




 


Inquiry

TITLE
NAME
EMAIL
MESSAGE
CODE 
 
Cuzi Wood Techenology Co.,Ltd.
ADD:Huangqiao Villige,Sanbao Town,Xuzhou City,China
Contact:Seller
Email:plywood@cuzicn.com
http://www.xzcuzi.com/
 
Whatsapp:086 158 6211 3323
Wechat:086 158 6211 3323
Skype:louzcn
QQ:532304720
TAGS
PLYWOOD FILM FACED PLYWOOD
MARINE PLYWOOD COMMERCIAL PLYWOOD
VENEER PLYWOOD MDO PLYWOOD
MDO PLYWOOD

© 2009-2015 

  Sitemap